Stantuf 900 High Strength Low Alloy Steel Plate Manufacturer & Supplier
Stantuf 900 is a quenched & tempered high strength low alloy (HSLA) plate with a minimum yield strength of 900 MPa. Low carbon and micro-alloying give excellent weldability and formability at a far better strength-to-weight ratio than mild steel.
UNS: 900 MPa min | Category: High Tensile & High Strength Plate
Size Range
Outer Diameter: Thickness 3-80 mm (to 100 mm on enquiry) · Width 1250-3000 mm · Length 4000-12000 mm
Wall Thickness: 3 - 80 mm
Chemical Composition (%)
| C | Mn | Si | P | S | Micro-alloying |
|---|---|---|---|---|---|
| 0.20 max | 1.60 max | 0.50 max | 0.020 max | 0.010 max | Ni, Cr, V, Mo, Ti, Nb in small amounts |
Mechanical Properties
- Yield Strength Rp0.2
- 900 MPa min
- Tensile Strength Rm
- 940 - 1100 MPa
- Elongation A (GL 80 mm, t < 3 mm)
- 11% min
- Elongation A (5.65√So)
- 12% min
- Charpy V-notch
- 27 J min @ -20 °C (EN 10045-1)
Physical Properties
- Density
- 7.85 g/cm3
- Modulus of Elasticity
- 210 GPa
- Thermal Conductivity
- 40 W/m-K (20 C)
- Specific Heat
- 460 J/kg-K
- Coeff. of Thermal Expansion
- 12 um/m-C (20-200 C)
- Magnetic
- Ferromagnetic
Applicable Standards
- AS/NZS 3678
- EN 10051 (tolerances)
- EN 10045-1 (Charpy V-notch)
Applications
- Heavy road vehicles & trailers
- Crane booms & jibs
- Storage vessels
- Power plant structures
- Offshore structures
- Mining equipment frames
- Lifting & material handling equipment
Industries Served
- Heavy Vehicle & Trailer
- Cranes & Lifting
- Power & Energy
- Offshore & Marine
- Mining Equipment
- Construction
Key Advantages
- Replaces mild steel at roughly half the section for the same strength
- Charpy toughness held to 27 J at -20 C
- Good bendability for chassis, booms and box sections
- Produced to AS/NZS 3678 and EN 10025-6 practice
- Weight saved comes straight back as payload
Equivalent Grades
- EN 10025-6
- S890QL / S960QL
- SSAB
- Strenx 900 / Weldox 900
- ThyssenKrupp
- XABO 890